| model:7038（Filling-free high temperature edge banding hot melt adhesive） | |||||||
| Appearance： | Oval particles, light yellow transparent state, non-toxic and environmentally friendly。 | ||||||
| Technical Parameters： | 62000±10000mpa.s when the viscosity value is 200℃ | Density 0.98g/cm3 | |||||
| Softening Point90-98℃ | Anti-hot spot＞70℃ | ||||||
| Operating parameters： | Material humidity＞15℃ | Ambient temperature＞15℃ | Material moisture content8%-10% | Glue tank temperature160-180℃ | |||
| Operating temperature180-210℃ | pressure3-5kg/cm3 | Feeding speed＞20米/分钟 | |||||
| Scope of use： | Suitable for large-scale automatic linear edge banding machine; suitable for PVC, ABS, veneer, wood strip and other edge banding materials； | ||||||
| Large-scale automatic edge banding machine suitable for material feeding speed of 20-25 m/min; imported large-scale automatic edge banding machine | |||||||
| product features： | 1.Good transparency and low density。 | 2.High heat resistance, high strength, low temperature resistance, fast curing。 | |||||
| 3.Good fluidity, thin glue line, low glue consumption。 | 4.A small amount of glue can also achieve a strong bonding effect。 | ||||||
Use hot melt adhesive method and matters needing attention:
1. To understand and master the various models and technical performance (including technical parameters) of hot melt adhesives.
2. The temperature of the hot melt glue tank should be controlled within the operating temperature range.
3. Clean the preheated glue pot regularly to keep the glue pot clean.
4. Plates and edge banding materials should be protected from contamination.
5. The moisture content of wood should be around 8%-10%.
6. The amount of glue in the glue pot should be properly controlled. If the amount is too much, the glue will melt in turns, which will cause deterioration and aging, lower viscosity, and affect adhesion.